Stabilization of organic material with stabilizers containing a substituted phenol group



United States Patent 14 Claims. (Cl. 25247.5)

This application is a divisional application of our earlier filed application Ser. No. 276,191, filed Apr. 29, 1963 now US. Patent No. 3,282,939 granted Nov. 1, 1966, which in turn is a continuation-in-part application of our co-pending application Ser. No. 148,939, filed Oct. 30, 1961, now abandoned.

This invention relates to the stabilization of polyolefins, e.g. polypropylene, and/or other unstable organic ma terial with stabilizers containing a substituted phenol group. The invention also relates to a method of preparing stabilized polyolefins, e.g. polypropylene, and/or other organic material subject to degradation due, for eX- ample to oxidation in air, thermal degradation, or deterioration due to radiant energy such as visible and/ or ultraviolet light.

More specifically, the invention pertains to stabilization of polypropylene and/ or other organic material normally subject to oxidative, thermal and/or light induced deterioration with a stabilizer of the formula:

s \R wherein A is an alkylene group (straight or branched) chain)especiallylower alkylene, i.e. having up to 6 carbon atoms, e.g. methylene, ethylene, propylene, butylene, pentylene, hexylene, with structures-such as H2 CH2CHa-, CH, -CHzCHCHz-,

H3 H! CH;

R is a tertiary alkyl group, e.g., of 4 to 18 carbon atoms,

preferably a tertiary butyl group;

R represents one or more alkyl groups, e.g., of from 1 to 18 carbon atoms, especially from 1 to 8 carbon atoms, or hydrogen; but in the case of a tertiary alkyl group it is understood that bulky groups such as the tertiary butyl group are not contemplated in positions adjacent to one another in the phenyl nucleus;

R is a alkyl group, preferably having from 1 to 24 carbon atoms, or an alkylphenyl, or an alkylbenzyl group, said alkylphenyl or alkylbenzyl group having preferably 7 or 8 to 24 carbon atoms, especially dodecylphenyl or dodecylbenzyl, or hydrogen or hydroxyalkyl, preferably hydroxyloweralkyl;

R is an alkyl group, preferably having from 1 to 24 carbon atoms, or an alkylphenyl, or an alkylbenzyl group, said alkylphenyl o'r alkylbenzyl group having preferably 7 or 8 to 24 carbon atoms, especially dodecylphenyl or dodecylbenzyl, but in the case of tertiary alkyl groups or other bulky groups, R and R cannot both besuch bulky groups; or (alkylthio)-lower alkylene, especially having from 2 to 20 carbon atoms; or

(di-lower a1kylamino)-lower alkylene, especially hav- 3,338,833 Patented Aug. 29, 1967 wherein R R and A are defined as above, and A is defined the same as A;

R and R taken together may be a cyclic radical such as a heterocylic radical-preferably morpholinoso that R, and R when joined to the nitrogen of the Formula I, form said cyclic radical.

Thus it is seen that the compounds of the Formula I may contain a carboxamido group derived from a carboxyl group and a substituted amino group, such as monoor dialkylarnino, preferably having from 1 to 36 atoms, e.g., methylor dimethylamino, ethylor diethylamino, propylor dipropylamino, butylor dibutylamino, pentylor dipentylamino, hexylor dihexylamino, heptylor diheptylamino, octaylor dioctylamino, nonylor dinonylamino, decylor decyloctylamino, undecylamino, dodecylamino, didodecylamino, tridecylamino, tetradecylamino, pentadecylamino, hexadecylamino, heptadecylamino, octadecylamino, etc.

Accordingly, it is a prime object of the invention to provide stable organic material, e.g., stable polymeric material, preferably polypropylene. In this specification it is understood that polymeric material means polyolefins such as polyethylene, etc. Preferably the polyolefins are of high molecular weight, e.g., above 1000 into the hundreds of thousands range. The polyethylenes and polypropylenes may be of high density, medium density or low density class.

Polymeric materials such as the foregoing find use as thermoplastic molding or coating agents. Moreover, because of their high dielectric strength and their resistance to water, they are particularly useful as insulators or dielectrics in condensers and other such equipment. It is known that these polyolefins, e.g. polyethylene and polypropylene, are attacked by oxygen, particularly when eX- posed to the atmosphere and at elevated temperatures. For example, during use or manufacture the desirable properties of the polyolefins may be impaired due to oxidative deterioration. Such degradation causes loss in dielectric properties, discoloration, embrittlement, gelation, etc.

Not only homopolymeric material, but also copolymers and physical mixtures thereof are stabilized according to the present invention. For example, high impact polystyrene containing copolymers of butadiene and styrene are stabilized according to the invention.

The invention is also particularly useful in stabilizinglubricating oils of various types including aliphatic esters such as e.g., dihexyl azelate, di-(Z-ethylhexyl) azelate, di-(3,5,5 trimethylhexyl)glutarate, di(3,5,5-tri methylpentyl)glutarate, di-(2 ethylhexyl)pimelate, di- (2 ethylhexyl)adipate, diisoamyl adipate, triamyl tricarballylate, pentaerythritol tetracaproate, dipropylene glycol dipelargonate, 1,5 pentanediol-di-(2-ethylhexanoate), etc.

The present invention also relates to the stabilizing of fatty materials including oils of animal and vegetable origin which tend to deteriorate on standing and exposure to atmospheric oxygen. Among the edible fats and oils within the scope of the present invention are: linseed oil, menhaden oil, cod lever oil, castor oil, olive oil, rapeseed oil, coconut oil, palm oil, corn oil, sesame oil, peanut oil, cotton seed oil, butter, fat, lard, beef tallow, etc. Other oils and fats which deteriorate on standing and exposure to oxygen in the air or oxygen at elevated temperatures are all within the scope of the present invention.

Within the scope of the invention also are saturated and unsaturated hydrocarbons which tend to deteriorate on storage such as, e.g., gasolines, both natural and synthetic, in particular, saturated and unsaturated gasolines, etc.; jet fuel; diesel oil; mineral oil; fuel oil; drying oil; waxes; resins; etc. Such hydrocarbons are protected against gum formation, discoloration and other deterioration with the stabilizers of the present invention.

It is furthermore an object of the present invention to provide novel substituted amide compounds which are versatile and effective stabilizers in at least a single class of the foregoing organic materials which are normally subject to deterioration caused by exposure to light and/ or heat and/ or oxygen, etc.

A particularly preferred stabilizer of the invention is N,N-di-n-dodecyl 3,5 di-t-butyl-4-hydroxyphenylacetamide, which is especially useful in tabilizing polyolefinic material, e.g. polypropylene and polyethylene, as well as other polymeric material, e.g. polystyrene, in particular, high impact polystyrene. This stabilizer is also an effective stabilizer for other relatively unstable organic material, e.g. hydrocarbon oil of mineral origin, in particular, mineral oil; gasoline, both natural and synthetic; oils of animal origin, in particular, lard; oils of vegetable origin, in particular, peanut oil; high temperature lubricating oils, e.g. diesters of fatty acids, in particular, diesters of fatty acids having from 5 to carbon atoms per molecule. Further organic materials which are effectively stabilized by this compound comprise: aldehydes, e.g. aliphatic, such as heptaldehydes.

It is understood that the stabilizers of the invention are not necessarily of equivalent potency. The specific stabilizer most useful to a given unstable material will depend upon several factors for its advantages. Availability and cost of raw materials for the manufacture of the stabilizer and effective inhibitory action of the stabilizer including duration and degree of activity are among the factors which control the choice of a specific stabilizer for a specific substrate which is normally subject to deterioration. Toxicity, color, stability to light and/ or heat and solubility are also important factors. For example, preferred compositions according to the invention comprise from about 0.001% to about 5% by weight of either N,N-di-n-dodecyl-3,S-di-t-butyl 4 hydroxyphenyl acetamide, or N-n-octadecyl-fi-(3,5-di-t-butyl 4 hydroxyphenyl) propionamide, or N-n-octadecyl-B,5-di-t-butyl-4- hydroxyphenylacctamide, and poly-propylene.

In general, stabilizers of the invention are employed in a concentration of from about 0.001% to about 5% by weight, preferably from about 0.01% to about 1% by Weight. The specific concentration used varies with the substrate and the stabilizer, but the following ranges are preferred.

Concentrations of about 0.001% to about 1% by weight for the stabilizer in polyethylene are useful. In polypropylene from about 0.05% to about 1% by weight of stabilizer is especially useful. For polystyrene from about 0.1% to about 1% by Weight is useful. In mineral oils, concentrations of from about 0.005% to about 1% by weight of stabilizer are used. Gasolines are stabilized with from about 0.01% to about 0.1% by weight of stabilizer, preferably about 0.05 by weight. Fatty material of animal origin such as lard is stabilized with from about 0.001% to about 0.1% by weight of stabilizer. Oils of vegetable origin such as cotton seed oil are similarly l stabilized with from about 0.001% to about 0.1% by weight of stabilizer.

Hydrocarbon material such as cycloolefins, e.g. cyclohexene, is advantageously stabilized with from about 0.001% to about 1% by weight of the stabilizers of the present invention. Similar concentrations of stabilizer are used to stabilize aldehydes such as, e.g., about 0.001% by weight in heptaldehyde. High temperature lubricants which are essentially diesters, e.g. diisoamyladipate, are stabilized with from about 0.5% to about 5%, preferably about 2%, by weight of a stabilizer according to the invention.

The compounds of this invention may be used also to stabilize organic material in combination with other additive agents such as, e.g., antioxidants, pourpoint depressants, corrosion and rust inhibitors, dispersing agents, demulsifiers, antifoaming agents, carbon black, accelerators and other chemicals used in rubber compounding, plasticizers, color stabilizers, heat stabilizers, ultraviolet absorbers, dyes, pigments, metal chelating agents, etc.

A particularly useful stabilizer system for polymeric material comprises a stabilizer of the Formula I and dilauryl-beta-thio-di-propionate (hereinafter referred to as DLTDP). Generally from about 0.005% to about 10% (based on the stabilized composition) by weight of DLTDP and other stabilizers, e.g. of the Formula I, are employed. Polypropylene is advantageously stabilized with about 0.5% by weight of DLTDP and 0.5% by weight of a stabilizer of the Formula I.

In place of DLTDP, other similar diesters are usefully employed with the stabilizers of the Formula I for stabilization of organic material, e.g., polypropylene. Such diesters as the following are useful:

wherein n is a small number, e.g. 1 or 2; and R and R are each independently an alkyl group, e.g.

having 8 to 24 carbon atoms.

The amide stabilizer compounds of the invention are prepared in a number of ways. Thus, for example, these amid-es are prepared by reaction of the acid chloride precursor compound with the appropriate amino or morpholino, etc., moiety. The reaction is carried out advantageously in the presence of a hydrogen chloride acceptor such as, e.g., triethylamine. These amides may also be prepared by conventional methods as, e.g., by the reaction of an alkylamide and the appropriate precursor acid.

The following reaction schemes illustrate several methods of preparing the compounds of the invention.

R is a hydroxyphenyl monoor dialkyl-substituted radical;

n is a small whole number, e.g. 1 or 2;

R is hydrogen or alkyl;

R is hydrogen or alkyl;

R is alkyl;

R and R taken together can represent e.g. alkyleneoxyalkylene to make a morpholino radical.

Although the foregoing hindered phenol acids, esters, acyl halides, etc. illustrate especially useful methods of preparing the compounds of the invention, nevertheless other substituted phenols are useful too, e.g., of the Formula III:

compounds R2 III wherein Other starting materials include primary or secondary amines having alkyl groups (including tertiary alkyl groups, e.g. t-butyl) such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, etc., or amines having alkaryl, aralkyl, alkylarylalkyl groups, etc. The following examples are illustrative of the invention only, and there is no intention to limit the scope of the invention thereto. In the following examples parts are by weight, unless otherwise specified, and temperature is in degrees centigrade. The relationship between parts by weight and parts by volume is as grams to cubic centimeters. 7

Example 1.-N-n=oetadecyl-3,5-di-t-butyl-4-hydroxyphenylacetamide 8.1 parts of octadecylamine and 3.0 parts of triethylamine are dissolved in 70 parts by volume of dry benzene, and 8.6 parts of 3,5-di-t-butyl-4-hydroxyphenylacetyl chloride, dissolved in 20 parts by volume of dry benzene, are added dropwise at 35 over a period of 10 minutes. The reactants are heated under reflux for 3 hours. 4.2 parts of triethylamine hydrochloride are filtered off, and the clear filtrate is washed with distilled Water and with saturated sodium bicarbonate solution, dried over anhydrous sodium sulfate, and the solvent is removed by distillation at about mm. Hg pressure. The residue weighs 16 parts and is dissolved in 60 parts by volume of 3060 petroleum ether and cooled for crystallization. The crystalline precipitate is filtered and dried, melting at 72-76. The product N-n-octadecyl-3,5-di-t-butyl-4-hydroxyphenylacetamide is obtained in yield of 12.2 parts and is recrystallized from a mixture of 200 parts by volume of acetonitrile and 30 parts by volume of ethanol, melting at 79-81.

' If in Example 1, 7.9 parts of dodecylaniline are substituted for octadecylamine, then N-dodecylphenyl-3,5-di t-butyl-4-hydroxyphenylacetamide is obtained.

If in Example 1, 8.3 parts of dodecylbenzylamine are substituted for octadecylamine, then N-dodecylbenzyl-3,5- di-t-butyl-4-hydroxyphenylacetamide is obtained.

If in Example 1, 3.9 parts of tertiary-octylamine are substituted for octadecylamine, then N-t-octyl-3,5-di-tbutyl-4-hydroxyphenylacetamide is obtained. Tertiaryoctylamine has the formula:

CH (1H CHa-(il-CHs-C-NH:

CH CH3 Example 2.-3,5-di-t-butyl-4-hydroxyphenylacetomvrpholide 4.1 parts of morpholine and 4.85 parts of triethylamine are dissolved in 60 parts by volume of benzene, and 12.7 parts of 3,5-di-t-butyl-4-hydroxyphenylacetyl chloride, dissolved in 20 parts by volume of benzene, are added dropwise at 37 over a period of 10 minutes. The reactants are heated under reflux for 2 /2 hours. 5.9 parts of tri- 'ethylamine hydrochloride are filtered 011, and the filtrate is washed with water and with saturated sodium bicarbonate solution, dried over anhydrous sodium sulfate, and the solvent is evaporated under vacuum. The distillation Example 39-111mm (Z-ethylhexyl)3,5-di-t-butyl-4- hydroxyphenylacetamide 7.2 parts of freshly distilled di-Z-ethylhexylamine and 3 parts of triethylamine are dissolved in 60' parts by volume of benzene and 8.6 parts of 2,6-di-t-butyl-4-hydroxyphenylacetyl chloride, dissolved in 20 parts by volume of benzene, are added dropwise at 23 over a period of 10 minutes. The reactants are heated under reflux for 2 /2 hours, 3.5 parts of triethylamine hydrochloride are filtered and the benzene filtrate is washed first With Water, then with saturated sodium bicarbonate solution, dried over anhydrous sodium sulfate, and the solvent removed by distillation at 15 mm. Hg pressure. The residue (14.7 parts) is purified by column chromatography using silica gel as packing. 10.5 parts of N,N-bis-(2-ethylhexyl)-3,5- di-t-butyl-4-hydroxyphenylacetamide are obtained as a viscous oil.

Analyris.Calculated for C32H57NO2 (M.W. 487.79): C, 78.78%; H, 11.79%; N, 2.87%. Found: C, 78.96%; H, 11.88%; N, 3.10%.

Example 4.N-n-octadecyl-/3-(3,5-di-t-butyl-4-hydroxyphenyl)propi0namide Octadecylamine (4.18 parts) is heated with stirring at 155 for 4 hours with 4.32 parts of fi-(3,5.-di-t-butyl- 4-hydroxyphenyl)propionic acid, prepared from 2,6-di-tbutyl-p-cresol according to a series of reactions described by Coflield et al., J. Am. Chem. Soc. 79, 5022-5023 (1957). At the end of this heating period, titration of the reaction mixture for acidity indicates thereaction is 84% complete. The waxy solid (8.5 parts), obtained when the reaction mixture is cooled to room temperature, is recrystallized from methanol, yielding 5 parts of N-noctadecyl ,8 (3,5 di t butyl 4 hydroxyphenyl)propionamide, as an off-white powder, melting at 82-84.

Example 11.Stabilizati0n of polypropylene hydoocyphenylacetam'ide 8.9 parts of di-n-dodecylamine and 3.1 parts of triethylamine are dissolved in 60 parts by volume of dry ben- Zone and 7.2 parts of 3,5-di-t-butyl-4-hydroxyphenacy1 chloride, dissolved in 20 parts by volume of dry benzene, are added dropwise with stirring at 35 over a period of 1-0 minutes. The temperature rises to 4 and the reactants are then heated at reflux for 3 hours. 3.6 parts of triethylamine hydrochloride are filtered 01f. The clear, red filtrate is washed twice with saturated sodium bicarbonate solution, once with saturated sodium chloride solut-ion, dried over anhydrous sodium sulfate, and the solvent evaporated under vacuum. 15.5 parts of a dark oil are obtained. The oil is purified by elution chromatography on silica gel. Mixtures of hexane and benzene, and chloroform and benzene are used as eluants. 5.0 parts of N,N-di- (n-dodecyl)-3,5-di-t-butyl-4- ydroxyphenylacetamide are obtained as a light brown oil.

Analysis.Calculated for C H O N: C, 80.06%; H, 12.26%; N, 2.33%. Found: C, 80.32%; H, 12.23%; N, 2.40%.

Example 6.N-(n-octadecylthiaethyl)-3-(3',5'-ditert.butyl-4'-hydroqcyphenyl) propionamide 11.0 parts of 2-aminoethyl-n-octadecylsulfide and 4.04 parts of triethylamine are dissolved in parts by vol- 17 V ume of dry benzene, and 10.7 parts of 3-(3',5'-di-tert. butyl-4'-hydroxyphenyl)propionyl chloride, dissolved in 100 parts by volume of dry benzene, are added dropwise at room temperature over a period of 45 minutes. The reactants are stirred at ambient temperature overnight. 7.1 parts of triethylamine hydrochloride are filtered off, and the filtrate treated as in Example 1. After drying over sodium sulfate, the benzene solution is filtered and stripped of solvent to give 16.3 parts of N-(n-octadecylthioethyl) 3 (3,5-di-tertbutyl-4'-hydroxyphenyl)propionamide. Repeated crystallization from hexane gives the product as a white solid of constant melting point 70-72.

6.5 parts of 3-(diethylamino)propylamine and 12.1 parts of triethylamine are dissolved in 100 parts by volume of dry benzene, and 17.8 parts of 3-(3',5'-di-tert. butyl-4-hydroxyphenyl)propionyl-chloride, dissolved in 200 parts by volume of dry benzene, are added dropwise at room temperature. The reactants are stirred at ambient temperatures overnight. 10.4 parts of triethylamine hydrochloride are filtered off and the filtrate treated as in Ex ample 1. After drying over sodium sulfate, the drying agent is removed and the solvent stripped to give 18.5 parts of N-(3"-diethylamino-n-propyl)-3-(3',5-di-tert.butyl-4-hydroxyphenyl)propionamide. This is purified by dissolving in 5% hydrochloric acid, adding zinc dust, filtering, basifying and extracting with ether. After washing with saturated sodium chloride, the ethereal solution is dried over sodium sulfate, filtered and stripped of solvent to give the product as a pale yellow oil which boils at 225-250 at 20-30 microns.

Analysis.Calculated for C H O N C, 73.80%; H, 10.84%; N, 7.17%. Found: C, 73.67%; H, 10.76%; N, 6.99%.

Example 8.N-2-hydr0xyethyl-N-laur0yl0xyethyl-3-(3', 5 '-di-tert.bmyl-4'-hydr0xyphenyl) propionamide 12.1 parts of N,Ndi-2-hydroxyethyl-3-(3',5'-di-tert.butyl-4'-hydroxyphenyl)propionamide and 12.1 parts of triethylamine are dissolved in 50 parts by volume of dry benzene, and 17.2 parts of lauroyl chloride added drop wise over a period of 0.5 hour while gently cooling the reaction vessel. The reactants are stirred at room temperature overnight. The resulting white solid is filtered off and the filtrate treated as in Example 3. After drying over sodium sulfate, the benzene solution is filtered and stripped of solvent to give 24 parts of N-2-hydroxyethyl- N-lauroyloxyethyl 3 (3,5-di-tert.butyl 4' hydroxyphenyl)prpionamide. Purification is achieved by chromatographing the product from 650 parts of alumina (neutral, activity 1). After washing the column with benzene, the product is eluted with 1:1 chloroform-benzene. Removal of the solvent gives the product as a hydrocarbon-soluble oil.

Analysis-Calculated for C H 7O N: C, 72.35%; H, 10.49%; N, 2.56%. Found: C, 72.57%; H, 10.69%; N, 2.36%.

Example 9.--4-phenyl-1,7-bis[,8-(3',5'-di-tert.butyl-4-hydroxyphenyl propz'ony l] diethylenetriamine 5.37 parts of anilino bis-(2-ethylamine) and 16.16 parts of triethylamine are dissolved in 200 parts by volume of dry benzene, and 21.4 parts of 3-(3,5'-di-tert.butyl-4'- hydroxyphenyl)propionyl chloride, dissolved in 150 parts by volume of dry benzene, are added dropwise over a period of 1.5 hours while gently cooling the reaction vessel. The reactants are stirred at room temperature overnight. The resulting White solid is filtered off and the filtrate treated as in Example 1. After drying over sodium sulfate, the benzene solution is filtered and stripped to give 19.6 parts of 4-phenyl-1,7-bis[B-(3,5-di-tert.butyl- 4-hydroxyphenyl) propionyl]diethylenetriamine. Several crystallizations from methylene dichloride yield the product as a white solid of constant melting point 184-185".

Example 10.N-lauroyl-N'-[3-(3',5-di-tert.butyl-4- hydroxyphenynpro pionyl] ethylenediamine 7.51 parts of N-aminoethyl lauramide and 5.05 parts of triethylamine are dissolved in parts by volume of dry benzene, and 12.5 parts of 3-(3,5-di-tert.butyl-4'- hydroxyphenyDpropionyl chloride, dissolved in 100 parts by volume of dry benzene, are added dropwise at room temperature over a 1.5 hour interval. The reactants are stirred at room temperature overnight. 3.6 parts of triethylamine hydrochloride are filtered off and the filtrate treated as in Example 1. After drying over sodium sulfate, the benzene solution is filtered and the solvent stripped under diminished pressure to give 15.7 parts of N lauroyl N [3-(3',5-di-tert.butyl-4-hydroxyphenyl)propionyl] ethylenediamine. Purification is achieved by first chromatographing the product through 167 parts of silica gel, washing the column with benzene, chloroform and finally eluting the product with acetone. Removal of the acetone leaves a residue, which after trituration with petroleum ether and crystallization from aqueous ethanol gives a white solid having melting point 122-124".

Example Il.-Stwbilizati0n of polypropylene Unstabilized polypropylene powder (Hercules Profax 6501) is thoroughly blended with 0.5% by weight of N,N di-(n-dodecyl)-3,5-di-t-butyl-4-hydroxyphenylacetamide, made according to Example 5 hereinabove. The blended material is then milled on a two roller mill at 182 for 5 minutes, after which time the stabilized polypropylene is sheeted from the mill and allowed to cool.

The milled polypropylene sheet is then cut into small pieces and pressed for 7 minutes on a hydraulic press at 218 and 2000 pounds per square inch pressure. The resultant sheet of 25 mil thickness is then tested for resistance to accelerated aging in a forced draft oven at 149. The resultant composition of 0.5% by weight of N,N-di- (n-dodecyl)-3,5-di-t-butyl-4-hydroxyphenylacetamide and polypropylene is stabilized against oxidative deterioration for 1000 hours. The unstabilized polypropylene deteriorates after only 3 hours.

In like manner as in this example, stabilized compositions of polypropylene are prepared having 0.5% by weight of a compound prepared according to each of the foregoing examples (l-10 inclusive).

In a similar manner as in this example, stable compositions of polypropylene are prepared with 0.5% by weight of one compound according to each of the preceding examples (1-10 inclusive) together with 0.5% by weight of di-lauryl-fi-thio-dipropionate. In some cases the improvement is so remarkable that a synergistic effect is observed in the oven-aging test.

Example 12.--Stabilization of mineral oil A water-white, refined (U.S.P. grade) mineral oil (Esso Primol D) is stabilized under the following test conditions.

A sample of mineral oil (10 parts) is placed in a Slightype oxidation flask filled with oxygen at room temperature (25) and atmospheric pressure. Thereafter, the flask is sealed to form a system having a mercury manometer which measures the pressure changes as oxygen is absorbed by the sample in the flask. The sample is then heated at 150 until the manometer registers a decrease of 300 mm. Hg pressure within the flask with reference to the maximum pressure obtained at 150. The stabilized mineral oil contains 0.1% by weight of N-n-octadecyl-fl- 3 ,5 -di-t-butyl-4-hydroxyphenyl) propionamide.

Example 13.--Stabilizati0n of a resin containing elastomer High impact polystyrene resin containing elastomer (i.e. butadiene-styrene) is stabilized against loss of elon- 9 gation properties by incorporation of 0.5% by weight of N-n-octadecyl-p-(3,5-di-t-butyl-4-hydroxyphenyl)propionamide. Under the test conditions described hereinbelow, the stabilized resin retains 85% of its original elongation properties, whereas the unstabilized resin re-' tains only 15% of its elongation properties.

The unstabilized resin is dissolved in chloroform and the stabilizer then added, after which the mixture is cast on a glass plate and the solvent evaporated to yield a uniform film which, upon drying, is removed and cut up, and then pressed for 7 minutes at a temperature of 163 and a pressure of 2000 pounds per square inch into a sheet of uniform thickness (25 mil). The sheets are then cut into strips, approximately 4 x 0.5 inches. A portion of these strips is then measured for length of elongation in the Instron Tensile tester (Instron Engineering Corporation, Quincy, Massachusetts). The remaining portion of the strips is aged in a forced draft oven for 6 weeks at 75 and thereafter tested for elongation.

A similar amount of N-n-octadecyl-3,5-di-t-butyl-4-hydroxyphenylacetamide also is effective in stabilizing high impact polystyrene (65% elongation retained, blank being 15 What is claimed is:

1. A composition of matter stabilized against deterioration which comprises organic material normally subject to deterioration and a stabilizing amount of a stabilizer compound of the formula:

wherein A is a member selected from the group consisting of lower alkylene and iso-lower-alkylene;

R is a tertiary alkyl group having 4 to 1-8 carbon atoms;

R is a member selected from the group consisting of alkyl, having from 1 to 18 carbon atoms, and hydrogen;

R is a member selected from the group consisting of (i) alkyl, having from 1 to 24 carbon atoms, (ii) hydrogen, (iii) CH CH when R; is the -CH CH O group, (iv) alkylphenyl, having 7 to 24 carbon atoms, (v) alkylbenzyl, having 8 to 24 carbon atoms, (vi) hydroxy-lo wer-alkyl;

R is a member selected from the group consisting (.15 (i) alkyl, having from 1 to 24 carbon atoms, (ii) CH CH O- when joined to N and to R to iorm the morpholino radical, (iii) alkylphenyl, having from 7 to 24 carbon atoms, (iv) alkylbenzyl, having from 8 to 24 carbon atoms, (v) (alkylthio)lower-alkyl, having 2 to 20 carbon atoms, (vi) (di-lower-alkyl-amino)lower alkyl, having 3 to 15 carbon atoms, (vii) (carbalkoxy) lower alkyl, having 3 to 14 carbon atoms, (viii) the group of the formula:

wherein R R and A are as defined above, and A is defined the same as A.

2. A composition of matter as claimed in claim 1 wherein the organic material is polypropylene and the stabilizer compound is N-n-octadecyl-3-5-di-t-butyl-4-hydroxyphenylacetamide.

3. A composition of matter as claimed in claim 1 wherein the organic material is mineral oil and the stabilizer compound is N-n-octadecyl-3-5-di-t-butyl-4-hydroxyphenylacetamide.

4. A composition of matter as claimed in claim 1 wherein the organic material is high impact polystyrene and the stabilizer compound is N-n-octadecy1-3-5-di-tbutyl-4-hydroxyphenylacetamide.

5. A composition of matter as claimed in claim 1 wherein the organic material is mineral oil and the stabilizer compound is N-n-octadecyl-p-(3,5-di-t-butyl-4-hydroxyphenyl)propionamide.

6. A composition of matter as claimed in claim 1 wherein the organic material is high impact polystyrene and the stabilizer compound is N-n-octadecyl-fl-(3,5-di-tbutyl-4-hydroxyphenyl)propionamide.

7. A composition of matter which comprises polyolefinic material, and a stabilizing amount of a stabilizer system consisting essentially of from about 0.005% to about 10% of di-lauryl-thiodipropionate and from about 0.005% to about 10% of a stabilizer compound of the formula:

11' /Ra H O: A0N\ wherein A is a member selected from the group consisting of lower alkylene and iso-lower-alkylene;

R is a terteriary alkyl group having 4 to 18 carbon atoms;

R; is a member selected from the group consisting of alkyl, having from 1 to 18 carbon atoms, and hydro- R is a member selected from the group consisting of (i) alkyl, having from 1 to 24 carbon atoms, (ii) hydrogen, (iii) CH CH when R; is the CH CH O group, (iv) alkylphenyl, having 7 to 24 carbon atoms, (v) alkylbenzyl, having 8 to 24 carbon atoms, (vi) hydroxy-lower-al-kyl;

R is a member selected from the group consisting of (i) alkyl, having from 1 to 24 carbon atoms, (ii) CH CH O when joined to N and R to form the morpholino radical, (iii) alkylphenyl, having from 7 to 24 carbon atoms, (iv) alkylbenzyl, having from 8 to 24 carbon atoms, (v) (alkylthio)lower-alky1, having 2 to 20 carbon atoms, (vi) (di-lower-alkylamino) lower alkyl, having 3 to 14 carbon atoms, (viii) the group of the formula wherein R R and A are defined the same as A.

8. A composition of matter as claimed in claim 1 wherein the organic material normally subject to deterioration is polypropylene, and including di-lauryl-fl-thiodipropionate.

9. A composition of matter as claimed in claim 1 wherein the organic material normally subject to deterioration is polystyrene, and including di-l-auryl-fi-thiodialso containing a stabilizing amount of di-lauryl-B-thiodipropionate.

10. A composition of matter as claimed in claim 2 and propionate.

11. A composition of matter as claimed in claim 1 wherein the organic material is polypropylene, the stabilizer is 3,S-di-t-butyl-4-hydroxyphenylacetomorpholide,

as defined above, and A is wherein the organic material is polypropylene, the stabilizer is N,N-di-(n-d odecyl)-3,5-di-t-butyl-4-hydroxyphenylacetamide and also containing a stabilizing amount of di-lauryl-B-thiodipropionate.

References Cited UNITED STATES PATENTS 11/1960 Young et a1 25251.5 11/1960 Cofiield 25251.5

DANIEL E. WYMAN, Primary Examiner. L. G. XIARHOS, W. H. CANNON, Examiners.

UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION Patent No. 3,338,833 August 29, 1967 John D. Spivack et a1.

It is hereby certified that error appears in the above numbered patent requiring correction and that the said Letters Patent should read as corrected below.

Column 2, line 29, for "octayl" read octyl column 3, line 4, for "lever" read liver column 4, line 7, for "0.001%" read 0.01% column 6, line 48, for "Example ll.-Stabilization of polypropylene hydoxyphenylacetamide", in italics, read Example 5.-N,NDi(n-dodecyl)-3,S-di-t butyl-4hydroxyphenylacetamide in italics; column 10, lines 71 and 72, for "A composition of matter as claimed in claim 2 and propionate" read A composition of matter as claimed in claim 2 and also containing a stabilizing amount of di-lauryl- B-thiodipropionate Signed and sealed this 30th day of July 1968.

(SEAL) Attest:

EDWARD M.FLETCHER,JR. EDWARD J. BRENNER Attesting Officer Commissioner of Patents 

1. A COMPOSITION OF MATTER STABILIZED AGAINST DETERIORATION WHICH COMPRISES ORGANIC MATERIAL NORMALLY SUBJECT TO DETERIORATION AND A STABILIZING AMOUNT OF A STABILIZER COMPOUND OF THE FORMULA:
 3. A COMPOSITION OF MATTER AS CLAIMED IN CLAIM 1 WHEREIN THE ORGANIC MATERIAL IS MINERAL OIL AND THE STABILIZER COMPOUND IS N-N-OCTADECYL-3-5-DI-T-BUTYL-4-HYDROXYPHENYLACETAMIDE. 